Nominal chemical composition % (according to standard EN 573-1) :
|
|
Si
|
Fe
|
Cu
|
Zn
|
Remarques
|
Other
|
Al
|
| Each |
Total |
| 0,4 |
0,7
|
5,0-6,0 |
0,3
|
0,2-0,6 Bi; 0,2-0,6 Pb
|
0,05
|
0,15
|
Reste |
|
|
Typical mechanical characteristics :
|
|
Spun bars (according to standard EN 755-2) :
|
|
State
|
Dimensions (mm)
|
Rm (MPa)
|
Rp0,2 (MPa)
|
A%
|
A50 %
|
|
Diam
|
Cote/plat
|
Mini
|
Mini
|
Mini
|
Mini
|
|
T4
|
<200
|
<60
|
275
|
125
|
14
|
12
|
|
T6
|
<75
75 a 200
|
<60
-
|
310
295
|
230
195
|
8
6
|
6
|
|
|
Spun tubes (according to standard EN-755-2) :
|
|
State
|
Dimensions mm
Ep. de paroi
|
Rm (MPa)
|
Rp0,2 (MPa)
|
A % mini
|
A50 % mini
|
|
mini
|
max
|
mini
|
max
|
|
T6
|
£ 25
|
310
|
-
|
230
|
-
|
6
|
4
|
|
|
Stretched bars (according to standard EN-754-2) :
|
|
State
|
Dimensions mm
|
Rm (MPa)
|
Rp0,2 (MPa)
|
A % mini
|
A50 % mini
|
|
Diameter (D)
|
Cote sur Plat ou Ep. (S)
|
mini
|
max
|
mini
|
max
|
|
T3
|
£ 40
40<D£ 50
50<D£ 80
|
£ 40
40<S£ 50
50<S£ 80
|
320
300
280
|
-
-
-
|
270
250
210
|
-
-
-
|
10
10
10
|
8
-
-
|
|
T8
|
£ 80
|
£ 80
|
370
|
-
|
270
|
-
|
8
|
6
|
|
|
Drawn tubes (according to standard EN-754-2) :
|
|
State
|
Dimensions mm
Ep. de paroi
|
Rm (MPa)
|
Rp0,2 (MPa)
|
A % mini
|
A50 % mini
|
|
mini
|
max
|
mini
|
max
|
|
T3
|
£ 5
5<e£ 20
|
310
290
|
-
-
|
260
240
|
-
-
|
10
8
|
8
6
|
|
T8
|
£ 20
|
370
|
-
|
275
|
-
|
8
|
6
|
|
|
Wires according EN 1301-2 :
|
|
State
|
Diameter Until et y compris
|
Rm (MPa)
|
Rp0,2 (MPa)
typical
|
A100 m % typical
|
|
mini
|
max
|
|
T3
|
18
|
310
|
-
|
295
|
6
|
|
T8
|
18
|
370
|
-
|
310
|
4
|
|
|
Properties (for information):
|
|
Corrosion :
|
| General corrosion index |
Not recommended
|
| Corrosion in industrial atmosphere |
Not recommended
|
| Corrosion in marine atmosphere |
Not recommended
|
| Corrosion in rural atmosphere |
Acceptable
|
| Corrosion under stress |
Not recommended
|
| Exfoliation index |
Acceptable
|
| Intercrystalline corrosion |
Acceptable
|
| Pitting index |
Not recommended
|
|
|
Anodisation :
|
| Bright anodizing |
Not recommended
|
| Anodisation de couleur |
Not recommended
|
| Hard anodizing |
Good
|
| Protective anodizing |
Acceptable
|
|
|
Deformation, machining :
|
| |
Work hardened
|
| Deformation a froid |
Not recommended a fortement Not recommended
|
| Deep drawing |
Not recommended
|
| Tensile strain |
Not recommended
|
| Repellency |
Fortement Not recommended
|
| Filability |
Good
|
| Machinability |
Excellent
|
|
|
Welding :
|
| Welding by electron beam |
-
|
| Gas welding |
Fortement Not recommended
|
| Arc welding |
Fortement Not recommended
|
| Welding par points |
Not recommended
|
| Brazing |
Not recommended
|
| Soft soldering |
Acceptable
|
|
|
Physical and elastic properties :
|
|
State
|
Elastic
|
Physicals
|
| |
E
|
G
|
n
|
Tsol
|
Tliq
|
Cp
|
a
|
r
|
rel
|
l
|
EC
|
|
MPa
|
MPa
|
-
|
°C
|
°C
|
J kg-1 K-1
|
µm m-1 K-1
|
kg m-3
|
nW m
|
W m-1 K-1
|
%IACS
|
|
T3 / T4
|
72500
|
27300
|
0.33
|
540
|
645
|
863
|
23
|
2840
|
44
|
152
|
39
|
|
T6 / T8
|
72500
|
27300
|
0.33
|
540
|
645
|
863
|
23
|
2840
|
38
|
172
|
45.5
|
|
| Legende : |
|
E
|
Elasticity module |
MPa |
|
G
|
Rigidity module |
MPa |
|
n
|
Poisson coefficient |
|
|
Tsol
|
Temperature de Solidity |
°C |
|
Tliq
|
Melting temperature |
°C |
|
Cp
|
Specific heat |
J kg-1 K-1 |
|
a
|
Coefficient of thermal expansion |
µm m-1 K-1 |
|
r
|
Density |
kg m-3 |
|
rel
|
Resistivity |
nW m |
|
l
|
Thermal conductivity |
W m-1 K-1 |
|
EC
|
Electrical conductivity |
%IACS |
|
| International equivalences : |
|
International
|
France
|
Germany
|
Grande Bretagne
|
Italie
|
Suisse
|
Espagne
|
|
AA
|
NFA
|
Ancient
|
DIN
|
WNR
|
BS
|
Ancient
|
UNI
|
Ancient
|
SNCH
|
UNE
|
|
2011
|
2011
|
AU5PbBi
|
AlCuBiPb
|
3.1655
|
-
|
FC1
|
9002/5
|
6362
|
AlCu6BiPb
|
L 3192
|
|
Suede
|
Russie
|
USA
|
Japon
|
Canada
|
Australie
|
Tchequoslovaquie
|
Finlande
|
Norvege
|
Hollande
|
|
SS
|
GOST
|
ASTM
|
JIS
|
Ancient
|
CSA
|
|
CSN
|
SFS
|
NS
|
|
|
4355
|
-
|
2011
|
A2011
|
-
|
28S / CB60
|
A2011
|
-
|
-
|
-
|
14/11
|
|